| Customization: | Available |
|---|---|
| Type: | TIG/MIG |
| Material: | Copper / Copper Alloy |
|
Still deciding? Get samples of US$ 1/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Copper alloy welding wire Silicon Bronze TIG Welding rod AWS A5.8 ERCuSi-A CuSi3 GTAW for argon arc welding
| CHEMICAL COMPOSITION(%) | |||||||||||||
| Standard | Class | Alloy | Cu | Al | Fe | Mn | Ni | P | Pb | Si | Sn | Zn | Other |
| ISO24373 | Cu6560 | CuSi3Mn1 | bal. | 0.02 | 0.5 |
0.5~ 1.5 |
- | 0.05 | 0.02 |
2.8~ 4.0 |
0.2 | 0.4 | 0.5 |
| GB/T9460 | SCu6560 | CuSi3Mn | bal. |
max 0.01 |
max 0.5 |
max 1.5 |
- | - |
max 0.02 |
2.8~ 4.0 |
max 1.0 |
max 1.0 |
max 0.5 |
| BS EN14640 | Cu6560 | CuSi3Mn1 | bal. | 0.01 | 0.5 |
0.5~ 1.5 |
- | 0.02 | 0.02 |
2.8~ 4.0 |
0.2 | 0.2 | 0.4 |
| AWS A5.7 | C65600 | ERCuSi-A | bal. | 0.01 | 0.05 | 1.5 | - | - | 0.02 |
2.8~ 4.0 |
1.0 | 1.0 | 0.50 |
| DIN 1733 | 2.1461 | SG-CuSi3 | bal. |
max 0.01 |
max 0.3 |
0.5~ 1.5 |
- |
max 0.02 |
max 0.02 |
2.8~ 4.0 |
max 0.2 |
max 0.2 |
max 0.4 |
| TRADE MARK | S211 |
| Equivalent to AWS | ERCuSi-A |
| Characteristics | Good mechanical properties
Good corrosion resistance
|
| Welding Method | GTAW
Argon arc welding
|
| Application | Used for TIG,Excellent for plain or coated steels.Also used for sufacing arears subjected to corrossion. |
| Physical Properties and Mechanical Properties: | |
| Solids-Temperature | 910ºC |
| Liquids-Temperature | 1025ºC |
| Density | 8.5kg/dm3 |
| Tensile Strength | 330-370N/mm2 |
| Elongation | 40% |
| Brinell Hardness | 80-95HB |
| Phosphor Bronze CUSN8P | |||||||||||||
| CHEMICAL COMPOSITION(%) | |||||||||||||
| Standard | Class | Alloy | Cu | Al | Fe | Mn | Ni | P | Pb | Si | Sn | Zn | Other |
| ISO24373 | Cu5210 | CuSn8P | bal. | - | 0.1 | - | 0.2 |
0.01~ 0.4 |
0.02 | - |
7.5~ 8.5 |
0.2 | 0.2 |
| GB/T9460 | SCu5210 | CuSn8P | bal. |
- |
max 0.1 |
- |
max 0.2 |
0.01~
0.4 |
max 0.02 |
- |
7.5~ 8.5 |
max 0.2 |
max 0.2 |
| BS EN14640 | Cu5210 | CuSn9P | bal. | - | 0.1 | - | - |
0.01~ 0.4 |
0.02 | - |
7.5~ 9.0 |
0.2 | 0.5 |
| AWS A5.7 | C52100 | ERCuSn-C | bal. | 0.01 | 0.10 | - | - |
0.10~ 0.35 |
0.02 | - |
7.5~ 9.0 |
0.2 |
0.50 |
| Physical Properties and Mechanical Properties: | |||||||||||||
| Solid-Temperature | 875ºC | Liquids-Temperature | 1025ºC | ||||||||||
| Density | 8.8kg/dm3 | Tensile Strength | 260N/mm2 | ||||||||||
| Elongation | 20% | Brinell Hardness | 80HB | ||||||||||
| Introduction: | |||||||||||||
|
Recommended for the welding of copper with Cu-Sn alloy.Best for the butt joining welding of brass with steel.Pre-heat suggested for the large size Products,and pulsed argon arc welding is recommended for multilayer hard facing on steel. |
|||||||||||||